Methods and apparatuses for removing polysilicon from semiconductor workpieces

ABSTRACT

Methods and apparatuses for removing polysilicon material from a semiconductor workpiece are disclosed. A particular method includes contacting a polishing pad with a semiconductor workpiece having a surface polysilicon material. The method also includes disposing a polishing liquid between the polysilicon material and the polishing pad. The polishing liquid contains an oxidizer that does not include metal elements. The method further includes moving at least one of the semiconductor workpiece and the polishing pad relative to the other while the semiconductor workpiece contacts the polishing pad and the polishing liquid. At least some of the polysilicon material is removed while the polysilicon material contacts the oxidizer in the polishing liquid, as at least one of the semiconductor workpiece and the polishing pad moves relative to the other.

TECHNICAL FIELD

The present disclosure relates to methods and apparatuses for removing polysilicon material from semiconductor workpieces.

BACKGROUND

Mechanical and chemical-mechanical polishing processes (collectively, “CMP”) remove material from the surfaces of semiconductor workpieces in the production of microelectronic devices and other products. For example, many conventional semiconductor workpieces include polysilicon as a component for forming conductive and/or semi-conductive microelectronic structures (e.g., plugs or damascene lines). These polysilicon structures are typically formed by depositing a blanket polysilicon layer on a workpiece and removing the excess polysilicon material external to the plugs or damascene lines using a CMP process.

One problem associated with polishing polysilicon is that it is difficult to efficiently clean the workpiece surface after polishing. It appears that particles (e.g., abrasive elements from a polishing liquid and/or a polishing pad, particles removed from the workpiece, or other contaminants) can be adsorbed to the workpiece surface after the polysilicon material has been removed. Such adsorption can be strong enough to render conventional physical treatments (e.g., de-ionized water rinsing, megasonification, and brush cleaning) ineffective for removing at least some of the adsorbed contaminants from the workpiece surface after polishing.

One approach to addressing this problem is to treat the workpiece surface with a chemical solution after polishing. The chemical solution typically includes organic surfactants, hydrogen fluoride, ammonia hydroxide, and/or other suitable chemical compounds. A drawback with this approach is that the additional chemical treatment adds to the cost of the overall manufacturing process and reduces the product throughput. A further drawback is that the chemical treatment may use compounds (e.g., organic surfactants) that are not environmentally friendly, and may therefore be costly to dispose of. Accordingly, there is a need for an efficient and cost-effective technique for removing polysilicon materials from semiconductor workpieces.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a partially schematic, cross-sectional side view of a portion of a rotary polishing machine suitable for conducting processes in accordance with embodiments of the disclosure.

FIG. 2 is a partially schematic cross-sectional side view of a portion of the polishing apparatus shown in FIG. 1.

FIG. 3A is a partially schematic cross-sectional illustration of an arrangement for disposing an oxidizing solution adjacent to a semiconductor workpiece in accordance with an embodiment of the disclosure.

FIG. 3B is a partially schematic cross-sectional illustration of a semiconductor workpiece after having a layer of polysilicon material removed in accordance with an embodiment of the disclosure.

FIGS. 4A-H are schematic cross-sectional illustrations of the surface chemistry of a semiconductor workpiece during a polishing process in accordance with embodiments of the disclosure.

FIG. 5 is a partially schematic illustration of an arrangement of multiple polishing apparatuses for removing polysilicon material from semiconductor workpieces in accordance with an embodiment of the disclosure.

DETAILED DESCRIPTION

Specific details of several embodiments of the disclosure are described below with reference to semiconductor workpieces and systems for processing the workpieces. The workpieces can include micromechanical components, data storage elements, optics, read/write components, or other features. For example, the workpieces can include workpieces having dies including SRAM, DRAM (e.g., DDR-SDRAM), flash-memory (e.g., NAND flash-memory), processor, imager, and/or other dies. Moreover, several other embodiments of the invention can have configurations, components, or procedures different than those described in this section. A person of ordinary skill in the art, therefore, will accordingly understand that the invention may have other embodiments with additional elements, or the invention may have other embodiments without several of the elements shown and described below with reference to FIG. 1-5.

A particular method for removing polysilicon material from a semiconductor workpiece includes contacting a polishing pad with a semiconductor workpiece having a surface polysilicon material. The method also includes disposing a polishing liquid between the polysilicon material and the polishing pad. The polishing liquid contains an oxidizer that does not include metal elements. The method further includes moving at least one of the semiconductor workpiece and the polishing pad relative to the other while the semiconductor workpiece contacts the polishing pad and the polishing liquid. As a result, at least some of the polysilicon material is removed while the polysilicon material is contacting the oxidizer in the polishing liquid, as at least one of the semiconductor workpiece and the polishing pad moves relative to the other.

Another particular method for polishing a semiconductor workpiece in a chemical-mechanical polishing process includes contacting a polishing pad and a polishing liquid with a portion of a semiconductor workpiece. The semiconductor workpiece has a polysilicon material at a surface facing toward the polishing pad, and the polishing liquid contains an oxidizer. The method also includes moving at least one of the semiconductor workpiece and the polishing pad relative to the other while the semiconductor workpiece contacts the polishing pad and the polishing liquid. At least a portion of the polysilicon material is removed from the surface of the semiconductor workpiece when at least one of the semiconductor workpiece and the polishing pad is moved relative to the other. The method further includes modifying an ability of the polysilicon material at the surface of the semiconductor workpiece to attract water, while removing at least a portion of the polysilicon material from the surface of the semiconductor workpiece.

FIG. 1 schematically illustrates a representative rotary CMP machine 110 on which the foregoing processes may be conducted. The CMP machine 110 can include a platen 120, a carrier head 130, and a polishing pad 140. The CMP machine 110 can also have an under-pad 125 between an upper surface 122 of the platen 120 and a lower surface of the polishing pad 140. A drive assembly 126 rotates the platen 120 (as indicated by arrow F) and/or reciprocates the platen 120 back and forth (as indicated by arrow G). Because the polishing pad 140 is attached to the under-pad 125, the polishing pad 140 moves with the platen 120 during polishing.

The carrier head 130 has a lower surface 132 to which a semiconductor workpiece 150 can be attached, or the workpiece 150 can be attached to a resilient pad 134 under the lower surface 132. The carrier head 130 can be a weighted, free-floating workpiece carrier, or an actuator assembly 136 can be attached to the carrier head 130 to impart rotational motion (as indicated by arrow J) and/or reciprocal motion (as indicated by arrow I) to the semiconductor workpiece 150.

In the illustrated embodiment, the rotary CMP machine 110 can also include an optional dispense conduit 144 for dispensing an oxidizing solution 162 onto the polishing pad 140. The oxidizing solution 162 can contain hydrogen peroxide (H₂O₂), an organic peroxide ROOR′ (R and/or R′=C_(x)H_(y), where x and y are positive integers), an organic hydroperoxide ROOH (R=C_(x)H_(y) where x and y are positive integers), other suitable oxidizers that do not include metal elements, and/or combinations of any of the foregoing compounds. For example, the oxidizing solution 162 can include a combination of hydrogen peroxide, di-methyl peroxide, di-ethyl peroxide, methyl-ethyl peroxide, di-tert-butyl peroxide, and/or other suitable peroxides and hydroperoxides.

The polishing pad 140, a polishing solution 160, and the oxidizing solution 162 define a polishing medium that mechanically and/or chemically-mechanically removes material from the workpiece surface. The polishing solution 160 can include abrasive particles and chemicals suspended and/or dissolved in a liquid carrier (e.g., water). The abrasive particles and chemicals etch and/or oxidize the workpiece surface. The polishing solution 160 can also be a “clean” nonabrasive solution without abrasive particles. In most CMP applications, abrasive slurries with abrasive particles are used on non-abrasive polishing pads, and clean non-abrasive solutions without abrasive particles are used on fixed-abrasive polishing pads. The polishing liquid 160 can have an alkaline pH. For example, the polishing liquid 160 can include an alkaline silica slurry having potassium hydroxide (KOH), sodium hydroxide (NaOH), tetramethyl ammonium hydroxide (N(CH₃)₄OH), and/or piperazine (C₄H₁₀N₂). In other embodiments, the polishing liquid 160 can include other constituents that provide the appropriate pH.

To polish the semiconductor workpiece 150 with the CMP machine 110, the carrier head 130 presses the workpiece 150 facedown against the polishing pad 140. More specifically, the carrier head 130 generally presses the semiconductor workpiece 150 against the polishing solution 160 on a polishing surface 142 of the polishing pad 140, and the platen 120 and/or the carrier head 130 moves to rub the workpiece 150 against the polishing surface 142. As the semiconductor workpiece 150 rubs against the polishing surface 142, the polishing medium removes material from the face of the workpiece 150. The polishing liquid 160 mixed with the oxidizing solution 162 can also modify the surface chemistry of the semiconductor workpiece 150 while the polishing medium removes material from the face of the semiconductor workpiece 150, as described in more detail later with reference to FIGS. 4A-H.

FIG. 2 is an enlarged schematic illustration of a portion of the apparatus 110 shown in FIG. 1. The semiconductor workpiece 150 can include a substrate material 151 (e.g., an oxide glass) having a substrate material surface 152. The semiconductor workpiece 150 can further include an aperture 153 extending from the substrate material surface 152. A polysilicon material 154 can be disposed in the aperture 153 and can extend over the substrate material surface 152 adjacent to the aperture 153. The polysilicon material 154 can include doped or un-doped polysilicon for forming a via, a damascene line, or other structures to electrically connect features within or on the substrate material 151. The semiconductor workpiece 150 can include an intermediate layer 155 between the substrate material surface 152 and the portion of the polysilicon material 154 disposed outwardly from the aperture 153. The intermediate layer 155 can include an anti-reflective coating, a stop layer, or another type of layer. In still further embodiments, the intermediate layer 155 can be eliminated.

As illustrated in FIG. 3A, the excess polysilicon material 154 external to the aperture 153 can be removed during polishing as the semiconductor workpiece 150 rubs against the polishing pad 140 in the presence of the polishing liquid 160. In one embodiment, the polishing solution 160 is premixed with the oxidizing solution 162. In another embodiment, the polishing liquid 160 is pre-dispensed on the semiconductor workpiece 150, and the dispense conduit 144 can subsequently dispense the oxidizing solution 162 onto the workpiece 150 so that the oxidizing solution 162 mixes with the polishing liquid 160 on the polishing pad 140 during processing. In still a further embodiment, described below with reference to FIG. 5, the semiconductor workpiece 150 can be moved from one polishing pad having a first polishing liquid 160 a that is not mixed with the oxidizing solution 162, to a second polishing pad having a second polishing liquid 160 b that is mixed with the oxidizing solution 162. In any of these embodiments, the polysilicon material 154 of the semiconductor workpiece 150 is exposed to a polishing liquid that contains the oxidizing solution 162 to modify the surface chemistry of the semiconductor workpiece 150.

As illustrated in FIG. 3B, the polysilicon material 154 can be removed to the level of the intermediate layer 155. In one embodiment, for example, when the intermediate layer 155 includes an antireflective coating, the material removal process can include removing the intermediate layer 155 to expose the substrate material surface 152. In another embodiment, the intermediate layer 155 can include a stop layer, and the material removal process can be halted upon exposing the intermediate layer 155. In still a further embodiment, as described above, the intermediate layer 155 can be eliminated, and the material removal process can continue through the polysilicon material 154 until the substrate material surface 152 is exposed.

FIGS. 4A-H illustrate stages in a representative process for removing polysilicon material from the workpiece 150 and modifying the surface chemistry of the workpiece 150. Even though only chemical actions are illustrated, the removal process of polysilicon can include mechanical and chemical actions, including synergistic actions. The process is not limited by theory, however, and in other embodiments, the process may be conducted in accordance with other mechanisms. In the illustrated embodiment, the semiconductor workpiece 150 is initially polished using a first polishing liquid 160 a for bulk material removal. The first polishing liquid 160 a does not contain an oxidizer. The semiconductor workpiece 150 is subsequently polished with a second polishing liquid 160 b that does include an oxidizer, which can be either premixed into the second polishing liquid 160 b prior to reaching the workpiece 150, or mixed with the second polishing liquid 160 b during the CMP process at the surface of the workpiece 150. In particular embodiments, the second polishing liquid 160 b can contain about 0.1% to about 1.0% by weight, about 0.001% to about 50.0% by weight, or other suitable concentration of hydrogen peroxide.

In other embodiments, the second polishing liquid 160 b can be eliminated. Instead, the first polishing liquid 160 a can be mixed with the oxidizing solution 162 prior to or during the CMP process. As a result, the process of polishing the workpiece 150 (e.g., for removing bulk material) and modifying its surface chemistry can occur generally simultaneously.

FIG. 4A is a cross-sectional schematic illustration of a portion of the workpiece 150, with a workpiece surface 157 exposed to the first polishing liquid 160 a after an overlaying layer (e.g., silicon dioxide, not shown) has been removed. The workpiece surface 157 is shown in phantom lines for clarity. The workpiece 150 includes a first layer 159 a and a second layer 159 b of polysilicon material at the workpiece surface 157. The first layer 159 a includes a first silicon atom 161 a, a second silicon atom 161 b, and a third silicon atom 161 c connected together with first and second Si—Si covalent bonds 163 a-b. The second layer 159 b includes a fourth silicon atom 161 d connected to the first silicon atom 161 a with a third Si—Si covalent bond 163 c. During polishing, it is believed that multiple reactions with water take place to dislodge silicon atoms from the workpiece surface 157. For example, the first and second silicon atoms 161 a-b can react with a first water molecule 165 a to form Si—OH and Si—H functional groups, respectively, by breaking the first covalent bond 163 a as follows: 2Si+H₂O→Si—H+Si—OH

As illustrated in FIG. 4B, the first and second silicon atoms 161 a-b are separated from each other. Then, the reaction with water can continue to separate the first silicon atom 161 a from other adjacent atoms. For example, the first silicon atom 161 a and the third silicon atom 161 c can react with a second water molecule 165 b to break the second covalent bond 163 b and attach another hydroxyl group to the first silicon atom 161 a as follows: Si+Si—OH+H₂O→Si—H+OH—Si—OH

As illustrated in FIG. 4C, the first silicon atom 161 a is now separated from both the second and third silicon atoms 161 b-c. Then, another reaction with water can occur between a third water molecule 165 c, the first silicon atom 161 a, and the fourth silicon atom 161 d in the second layer 159 b before the first silicon atom is removed from the workpiece surface 157 as follows: Si+OH—Si—OH+H₂O→Si—H+Si—(OH)₃

As illustrated in FIG. 4D, at the end of this reaction, the first silicon atom 161 a is now dislodged from the workpiece surface 157 because all of the covalent bonds between this atom and the adjacent silicon atoms are broken. At the same time, individual adjacent silicon atoms are converted into Si—H functional groups.

Reacting the neighboring silicon atoms with water in a similar fashion can dislodge the other atoms in the first layer 159 a from the workpiece surface 157. FIG. 4E illustrates the workpiece surface 157 after all of the atoms of the first layer 159 a of the polysilicon material have been removed. The second layer 159 b now includes a plurality of Si—H functional groups having silicon atoms individually connected to a hydrogen atom. It is believed that these hydrogen atoms can cause the workpiece surface 157 to be hydrophobic at least because these Si—H functional groups are not sufficiently polarized. The hydrophobic surface 157 can have poor contact with an adjacent cleaning agent (e.g., de-ionized water) so that adsorbed contaminants at the surface 157 may not be easily disengaged after the CMP process.

After being polished with the first polishing liquid 160 a, the semiconductor workpiece 150 can be polished with the second polishing liquid 160 b to remove additional polysilicon material. As illustrated in FIG. 4F, the second polishing liquid 160 b contains hydrogen peroxide (H₂O₂), which can oxidize the silicon atoms at the workpiece surface 157 to form water and silicon oxide (Si_(x)O_(y), where x and y are positive integers). The following reaction is an example reaction, the product of which is silicon dioxide (SiO₂), though other silicon oxide compounds may also be formed: H₂O₂+Si—H→H₂O+SiOH Hydrogen peroxide can also react with surface silicon to form surface silicon oxide as follows: 2H₂O₂+Si→2H₂O+SiO₂

FIG. 4G illustrates the workpiece 150 after reacting with hydrogen peroxide. The workpiece surface 157 now contains a plurality of Si—OH functional groups, and has released water into the second polishing liquid 160 b. It is believed that the Si—OH functional groups can at least reduce the hydrophobicity and/or increase the hydrophilicity of the workpiece surface 157 because the Si—OH functional groups are sufficiently polarized. As a result, the ability of the workpiece surface 157 to attract water molecules is modified, and the workpiece surface 157 now tends to be hydrophilic instead of hydrophobic.

As illustrated in FIG. 4H, the hydrophilic workpiece surface 157 can have improved wettability to the second polishing liquid 160 b, a cleaning agent (e.g., de-ionized water), or other water based solutions at least because the workpiece surface 157 is likely to form hydrogen bonds with water molecules in these water based solutions. The improved wettability can enable these water based solutions to carry away adsorbed contaminants from the workpiece surface 157.

The workpiece 150 can then be further polished when the wafer surface 157 undergoes additional reactions with water generally similar to those described above with reference to FIGS. 4A-D. The resulting Si—H functional groups from the reactions with water can be oxidized and the stages illustrated in FIGS. 4A-H can be repeated until a desired removal amount is achieved for the CMP process.

Several embodiments of the foregoing process can reduce the operating costs associated with polishing polysilicon material because expensive post-CMP chemical treatments can be avoided, and simple physical treatments can be used. For example, de-ionized water rinsing, megasonification, brush cleaning, and/or other simple mechanical treatments can now be used to clean the workpiece surface 157. Moreover, several embodiments of the process can improve the quality of the CMP process. As described above, using conventional techniques typically results in adsorbed contaminants (e.g., abrasive elements) on the workpiece surface 157 that cannot be easily removed because of the hydrophobicity of the workpiece surface 157. The contaminants can scratch or otherwise damage the workpiece surface 157 when the workpiece 150 is rubbed against the polishing pad 140. Thus, at least reducing the hydrophobicity of the workpiece surface 157 can improve the contact between the polishing liquid and the workpiece surface 157, and thus reduce the amount of adsorbed contaminants on the workpiece surface 157. As a result, the risk of damaging the workpiece surface 157 during polishing can be reduced.

Further, several embodiments of the process can improve the robustness of the CMP process. For example, adding an oxidizer to the polishing liquid can enable other process parameters (e.g., processing temperatures, pH, amount of polishing force, etc.) to have values outside of the operating ranges associated with conventional processes. By increasing the available operating ranges for these parameters, the processes may be less sensitive to perturbations in these parameter values.

In several embodiments of the process, the oxidizer does not include any metal elements. Metal elements, if included with the oxidizer, could cause silicon contamination that interferes with subsequent metal deposition and processing and/or impacts the electrical property (e.g., the semi-conductive property) of the workpiece. As a result, by using an oxidizer that does not include metal elements, the likelihood of silicon contamination can be reduced or eliminated.

Several embodiments of the process can be at least partially “self-cleaning.” It is believed that the Si—OH functional groups at the wafer surface 157 can undergo hydrolysis in a basic solution to become negatively charged as follows: H₂O+Si—OH→H₃O⁺+Si—O⁻ It is also believed that contaminants (e.g., abrasive particles) also typically have negatively charged surfaces in a basic solution. The negatively charged wafer surface 157 can thus repel the negatively charged contaminants and reduce the amount of contaminants aggregated, stuck, or otherwise adsorbed onto the wafer surface 157.

In one embodiment, the polysilicon material 154 is removed while remaining in contact with the same polishing pad 140 during the entire process (e.g., as shown in FIG. 2 and FIG. 3). In another embodiment, shown in FIG. 5, a first portion of the polysilicon material 154 can be removed at a first apparatus 510 a, and a second portion of the polysilicon material 154 can be removed at a second apparatus 510 b. Each apparatus 510 a, 510 b can include a platen 520 carrying a polishing pad 540 and a carrier 530 configured to support the semiconductor workpiece 150. In one embodiment, each apparatus 510 a, 510 b includes a polishing pad 540 having the same composition. In another embodiment, the polishing pad 540 of the first apparatus 510 a can be different than the polishing pad 540 of the second apparatus 510 b. In either embodiment, suitable polishing pads 540 are available from vendors including Rodel of Newark, Del. In either embodiment, the first apparatus 510 a can be configured to remove material from the semiconductor workpiece 150 with the first polishing liquid 160 a, and the second apparatus 510 b can be configured to remove material from the semiconductor workpiece 150 with the second polishing liquid 160 b. Accordingly, the first and second polishing liquids 160 a, 160 b can be kept separate from each other during processing. The chemical compositions of the polishing liquids can be maintained at controlled levels with relative ease.

From the foregoing, it will be appreciated that specific embodiments of the invention have been described herein for purposes of illustration, but that various modifications may be made without deviating from the invention. For example, the processes described with reference to the Figures are used to remove the polysilicon material 154 from the workpiece 150. In other embodiments, these processes can also be used to remove amorphous silicon or single grain silicon. In any of the processes described above, the polishing liquid 160 can include dilute Hydrogen Fluoride (HF), Ammonia Hydroxide (NH₄OH), or other types of cleaning agents in addition to the compounds described above. Certain aspects of the invention described in the context of particular embodiments may be combined or eliminated in other embodiments. For example, the dispense conduit 144 can be eliminated in some embodiments. Further, while features and/or characteristics associated with certain embodiments of the invention have been described in the context of those embodiments, other embodiments may also exhibit such features and/or characteristics, and not all embodiments need necessarily exhibit such features and/or characteristics to fall within the scope of the invention. Accordingly, the invention is not limited, except as by the appended claims. 

1. A method for removing material from a semiconductor workpiece, comprising: contacting a polishing pad with a semiconductor workpiece having a surface polysilicon material; disposing a polishing liquid between the polysilicon material and the polishing pad, the polishing liquid containing an oxidizer that does not include metal elements; moving at least one of the semiconductor workpiece and the polishing pad relative to the other while the semiconductor workpiece contacts the polishing pad and the polishing liquid; removing at least some of the polysilicon material while the polysilicon material contacts the oxidizer in the polishing liquid as at least one of the semiconductor workpiece and the polishing pad moves relative to the other; forming a workpiece surface after removing at least some of the polysilicon material from the semiconductor workpiece, the workpiece surface having adsorbed contaminants; and carrying away the adsorbed contaminants from the workpiece surface via deionized water rinsing.
 2. The method of claim 1 wherein disposing a polishing liquid includes disposing a polishing liquid that contains hydrogen peroxide.
 3. The method of claim 1 wherein disposing a polishing liquid includes disposing a polishing liquid that contains organic peroxide and/or organic hydroperoxide.
 4. The method of claim 1, further comprising oxidizing at least some of the polysilicon material while the polysilicon material contacts the polishing liquid.
 5. The method of claim 1 wherein removing at least some of the polysilicon material includes removing at least some of the polysilicon material to obtain an exposed surface that is hydrophilic.
 6. The method of claim 1 wherein disposing a polishing liquid includes disposing a polishing liquid premixed with the oxidizer.
 7. The method of claim 1 wherein disposing a polishing liquid includes pre-dispensing a polishing slurry between the polysilicon material and the polishing pad, the polishing slurry not including the oxidizer, and wherein the method further includes dispensing a solution onto the workpiece that mixes with the polishing slurry while moving at least one of the semiconductor workpiece and the polishing pad relative to the other, the solution including the oxidizer.
 8. The method of claim 1 wherein disposing a polishing liquid includes disposing a polishing liquid that contains about 0.1% to about 1.0% hydrogen peroxide by weight.
 9. The method of claim 1 wherein disposing a polishing liquid includes disposing a polishing liquid that includes from about 0.001% to about 50.0% hydrogen peroxide by weight.
 10. The method of claim 1 wherein removing at least some of the polysilicon material includes removing at least some of the polysilicon material from a filled recess.
 11. The method of claim 1 wherein removing at least some of the polysilicon material includes removing doped polysilicon.
 12. The method of claim 1 wherein the polishing liquid is a first polishing liquid, and wherein the method further includes disposing a second polishing liquid between the polysilicon material and the polishing pad and moving at least one of the semiconductor workpiece and the polishing pad relative to the other while the semiconductor workpiece contacts the polishing pad and the second polishing liquid, wherein the second polishing liquid does not contain an oxidizer.
 13. The method of claim 1 wherein the polishing liquid is a first polishing liquid and the polishing pad is a first polishing pad, and wherein the method further includes disposing a second polishing liquid between the polysilicon material and a second polishing pad and moving at least one of the semiconductor workpiece and the second polishing pad relative to the other while the semiconductor workpiece contacts the second polishing pad and the second polishing liquid.
 14. The method of claim 13, further comprising moving the semiconductor workpiece from a first apparatus having the first polishing pad to a second apparatus having the second polishing pad.
 15. A method for polishing a semiconductor workpiece in a chemical-mechanical polishing process, comprising: contacting a polishing pad and a polishing liquid with a portion of a semiconductor workpiece having a polysilicon material at a surface facing toward the polishing pad, the polishing liquid containing an oxidizer; moving at least one of the semiconductor workpiece and the polishing pad relative to the other while the semiconductor workpiece contacts the polishing pad and the polishing liquid; removing at least a portion of the polysilicon material from the surface of the semiconductor workpiece when at least one of the semiconductor workpiece and the polishing pad is moved relative to the other; forming a workpiece surface after removing at least a portion of the polysilicon material from the semiconductor workpiece, the workpiece surface having adsorbed contaminants; modifying an ability of the polysilicon material at the workpiece surface of the semiconductor workpiece to attract water, while removing at least a portion of the polysilicon material from the surface of the semiconductor workpiece; thereafter, contacting the workpiece surface of the semiconductor workpiece with de-ionized water; and carrying away the adsorbed contaminants from the workpiece surface in a manner at least facilitated by the modified ability of the polysilicon material at the workpiece surface to attract water.
 16. The method of claim 15 wherein the oxidizer includes at least one of hydrogen peroxide, an organic peroxide, and an organic hydroperoxide.
 17. The method of claim 15 wherein modifying an ability to attract water includes increasing hydrophilicity of the surface of at least some of the polysilicon material.
 18. The method of claim 15 wherein modifying an ability to attract water includes decreasing hydrophobicity of the surface of at least some of the polysilicon material.
 19. The method of claim 15 wherein modifying an ability to attract water includes reacting the oxidizer of the polishing liquid with the polysilicon material while removing at least a portion of the polysilicon material from the surface of the semiconductor workpiece.
 20. The method of claim 15 wherein contacting a polishing pad and a polishing liquid with a portion of a semiconductor workpiece includes contacting a polishing pad and a polishing liquid containing hydrogen peroxide with a portion of the semiconductor workpiece.
 21. The method of claim 15, further comprising cleaning the surface of the semiconductor workpiece without chemically treating the surface of the semiconductor workpiece after the chemical-mechanical polishing process is completed.
 22. The method of claim 15, further comprising cleaning the surface of the semiconductor workpiece using at least one of de-ionized water rinsing, megasonification, and brush cleaning after the chemical-mechanical polishing process is completed.
 23. A method for removing a polysilicon material from a semiconductor workpiece, the polysilicon material being at a first surface of the semiconductor workpiece, comprising: contacting the polysilicon material at the first surface of the semiconductor workpiece with a polishing liquid; reacting silicon atoms of the polysilicon material to form Si—H and Si—OH functional groups; dislodging silicon atoms carrying the Si—OH functional groups from the first surface of the semiconductor workpiece; oxidizing the Si—H functional groups while the silicon atoms carrying the formed Si—OH functional groups are dislodged from the first surface of the semiconductor workpiece, and thereby forming a second surface of the semiconductor workpiece containing at least some Si—OH functional groups; thereafter, contacting the second surface of the semiconductor workpiece with de-ionized water; attracting water molecules from the de-ionized water to the second surface of the semiconductor workpiece by forming a plurality of hydrogen bonds between the Si—OH functional groups at the second surface and the water molecules; and carrying away contaminants from the second surface of the semiconductor workpiece with the de-ionized water molecule.
 24. The method of claim 23, further comprising converting the Si—H functional groups of the polysilicon material into silicon oxide (SixOy, where x and y are positive integers) after the oxidizer reacts with the polysilicon material.
 25. The method of claim 23, further comprising converting the Si—H functional groups of the polysilicon material into silicon dioxide (SiO2) after the oxidizer reacts with the polysilicon material.
 26. The method of claim 23 wherein reacting the Si—H functional groups with an oxidizer includes reacting the Si—H functional groups with hydrogen peroxide.
 27. The method of claim 23 wherein reacting the Si—H functional groups with an oxidizer includes releasing water after the oxidizer reacts with the polysilicon material.
 28. A method for processing a semiconductor substrate, comprising: contacting a polishing medium with a semiconductor workpiece having a polysilicon material at a first surface, the polishing medium including a polishing pad and a polishing liquid containing an aqueous solution of hydrogen peroxide (H₂O₂), and the polysilicon material having a plurality of layers of silicon atoms; dislodging some of the silicon atoms in the polysilicon material via a reaction with water molecules in the polishing liquid as follows: Si+3H₂O→3Si—H+Si—(OH)₃ oxidizing the Si—H functional groups of the polysilicon material with the oxidizer as follows: H₂O₂+Si—H→H₂O+Si—OH forming a second surface with at least some of the silicon atoms of the polysilicon material dislodged from the semiconductor substrate, the second surface having adsorbed contaminants and a plurality of Si—OH functional groups; thereafter, contacting the second surface of the semiconductor substrate with de-ionized water; forming a plurality of hydrogen bonds between the Si—OH functional groups at the second surface and the water molecules in the de-ionized water; and carrying away the adsorbed contaminants from the second surface with the water molecules in the de-ionized water.
 29. The method of claim 28 wherein oxidizing the Si—H functional groups includes increasing hydrophilicity of the second surface of the semiconductor substrate.
 30. The method of claim 28 wherein oxidizing the Si—H functional groups includes decreasing hydrophobicity of the second surface of the semiconductor substrate. 